EVA Low Temperature Hot Melt Adhesive Web
EVA low temperature hot melt adhesive web provides medium elasticity and cost-effective bonding for heat-sensitive substrates, EVA and XPE foam, and selected textile laminations. Its open web structure provides discontinuous adhesive coverage while maintaining flexibility.
Product Overview
| Item | Parameter Description |
|---|---|
| Material | Ethylene vinyl acetate copolymer |
| Core Features | Low-temperature bonding, medium elasticity, cost-effective |
| Structural Advantages | Open web structure, discontinuous adhesive coverage, stable bonding performance |
| Application Scenarios | Bonding of heat-sensitive substrates, EVA and XPE foam, and selected lightweight textile laminates. |
Low-Temperature Bonding
Designed for relatively low-temperature processing, making it suitable for selected heat-sensitive substrates such as EVA and XPE foam.
Medium Elasticity
Provides moderate flexibility for laminates that require a balance between bonding performance and material movement.
Open Web Structure
Discontinuous adhesive coverage can help preserve airflow and softness in selected textile laminates compared with continuous adhesive coverage.
Hot-Melt Adhesive Mesh Web Series
Engineered for precision bonding across diverse applications. Explore our specialized mesh web solutions featuring varying polymers to meet your exact manufacturing specifications.
PA Hot-Melt Adhesive Mesh Web
Offers exceptional resistance to washing and dry cleaning. Ideal for premium textiles, garments, and complex fabric lamination demanding strong adhesion.
PES Hot-Melt Adhesive Mesh Web
Superior durability with outstanding dry cleaning resistance. Perfect for automotive interiors, water treatment, and industrial filtration systems.
TPU Hot-Melt Adhesive Mesh Web
Features outstanding elasticity, low-temperature flexibility, and a soft hand-feel. Highly recommended for sportswear, footwear, and performance apparel.
PP Hot-Melt Adhesive Mesh Web
Specialized for bonding low surface energy materials. Provides excellent chemical resistance and lightweight performance for industrial manufacturing.
Industrial Performance
& Technical Specifications
Multiple specifications are available, with customization options for mesh weight, width and other production requirements.
Model Specifications
| Model | Material | Elasticity | Melting Point (℃) | Mesh Weight (g/m²) | Width (mm) | Length (m) | Lamination Temp (℃) | Pressure (MPa) | Press Time (s) | Features |
|---|---|---|---|---|---|---|---|---|---|---|
| EW-60 | EVA | Medium Elasticity | 55–65 | 10-50 | 5–1600 | 5–2000 | 65–80 | 0.15 | 8–15 | Ultra low temperature Ultra soft |
| EW-70 | EVA | Medium Elasticity | 65–75 | 15-60 | 5–1600 | 5–2000 | 75–90 | 0.15 | 10–20 | General purpose Balanced performance |
Technical Parameters
| Test Item | Technical Parameter |
|---|---|
| Bonding Performance | Evaluate with the actual substrate combination |
| Wash Resistance | Confirm according to end-use requirements and test conditions |
| Solvent Resistance | Application-specific testing recommended |
| Processing Conditions | Temperature, pressure and dwell time should be optimized for the selected grade and substrates |
| Elasticity | Medium elasticity |
| Documentation | Relevant test reports available for selected grades; confirm before ordering |
Final lamination temperature, pressure, dwell time, peel strength, wash resistance and durability should be verified with the actual materials and defined test conditions.
Need a custom specification?
Multiple specifications and customization options are available. We can tailor elasticity, melting point, mesh weight and other parameters according to your production requirements.
Request Technical Data Sheet
Receive complete specifications and factory-direct pricing for EW-60 & EW-70.
Compatible Materials
Engineered for seamless bonding across a wide spectrum of industrial and consumer materials, ensuring superior adhesion and durability.
Application Scope
Providing high-performance, eco-friendly adhesive solutions tailored for 15+ global industries.
Foam Lamination
EVA/XPE foam mats, shoe insoles
Packaging Industry
Carton reinforcement, paperboard bonding
Light Apparel
Thin fabric interlining, lace adhesion
Home Textiles
Curtain headers, lightweight quilt lamination
Filtration Industry
Support layer for air filter media
Disposable Supplies
Non-woven masks, medical dressings
Performance Comparison:
EVA vs. Other Hot Melt Adhesive Webs
Selecting the right hot melt adhesive mesh is critical for your production line. EVA hot melt adhesive web is often selected for relatively low-temperature processing and cost-effective lamination. Its medium elasticity makes it suitable for selected substrates such as EVA and XPE foam. Compare the technical indexes below to find the right fit for your industrial application.
| Performance Index | EVA Mesh | TPU Mesh | TPE Mesh | PA Mesh | PES Mesh |
|---|---|---|---|---|---|
| Low Temperature Activation | ★★★★★ (55°C) | ★★☆☆☆ (110°C) | ★★☆☆☆ (100°C) | ★★☆☆☆ (120°C) | ★★☆☆☆ (125°C) |
| Soft Hand Feeling | ★★★★☆ | ★★★★★ | ★★★★★ | ★★★☆☆ | ★★★☆☆ |
| Air Permeability | ★★★★☆ | ★★★★☆ | ★★★★★ | ★★★★★ | ★★★★★ |
| 40°C Wash Resistance | ★☆☆☆☆ (5-8 cycles) | ★★★☆☆ (10+ cycles) | ★★★☆☆ (8+ cycles) | ★★★★☆ (15+ cycles) | ★★★★★ (20+ cycles) |
| Maximum Heat Resistance | 70°C | 90°C | 80°C | 110°C | 115°C |
| Adhesion to EVA/XPE Foam | ★★★★★ | ★★★☆☆ | ★★★☆☆ | ★★☆☆☆ | ★★☆☆☆ |
| Material Cost | Lowest | Medium | Medium | Medium-high | High |
Unsure which mesh fits your production?
Leverage our 10,000+ specifications and expert R&D team to find the perfect customized adhesive solution.
Selection Matrix Based on Substrate & Working Condition
Identify the optimal hot-melt adhesive mesh film engineered for your specific application requirements and substrates.
| Substrate A | Substrate B | Core Requirements | Recommended Model | Mesh Weight (g/m²) | Temp Suggestion | Notes |
|---|---|---|---|---|---|---|
| EVA Foam | EVA Foam Yoga Mat | Low temp, shrink-proof, soft texture | EW-60 | 15-25 | 65-70°C | Pressure ≤0.1 MPa |
| XPE Foam | Non-woven Car Heat Insulation Pad | Low VOC, resistant to 80°C transportation | EW-70 | 20-30 | 75-80°C | Ventilate to eliminate odor |
| Tissue Paper | Disposable Nursing Pad | Light weight, breathable, eco-friendly | EW-60 | 8-12 | 65-70°C | Ultra low pressure to avoid glue penetration |
| Corrugated Board | Small Packaging Box | Fast curing, solvent-free | EW-70 | 10-15 | 75-80°C | Press holding time less than 10s |
| PP Non-woven | Disposable Mask Fabric | Hypoallergenic, low temperature processing | EW-60 | 8-10 | 65-70°C | Corona treatment for PP surface in advance |
| Thin Polyester Fabric | PE Protective Film | Tight sealing, lightweight design | EW-70 | 10-15 | 75-80°C | Prevent film melting damage |
| Shoe Synthetic Leather | EVA Midsole | Low temp processing to avoid EVA damage | EW-70 | 25-35 | 80-85°C | Polish EVA bonding surface beforehand |
Need a specialized bonding solution?
Our R&D team provides custom formulations and professional back coating services.
Quantitative Performance Data
& Long-term Reliability Verification
Comprehensive testing results and reliability verifications for hot-melt adhesive mesh films under rigorous industrial conditions.
Peel Strength Decline After Repeated Washing
Specimen: EW-70, 25 g/m²
Base Material: Double non-elastic polyester fabric
Lamination Parameter: 80°C / 0.15 MPa / 12 s
Test Criterion: ASTM D1876 T-type peeling test
Washing Standard: 40℃ household washing, standard detergent, 45 minutes per cycle
| Washing Cycles | Peel Strength (N/25mm) | Strength Retention | Hand Feeling Change | Bonding Condition |
|---|---|---|---|---|
| 0 Original | 14.5 | 100% | Soft | Intact bonding |
| 3 | 11.2 | 77% | Slightly stiff | Minor edge separation |
| 5 | 8.5 | 59% | Noticeable hardening | Partial delamination |
| 8 | 5.0 | 34% | Hard and brittle | Large-area peeling |
| 10 | 2.5 | 17% | Severe hardening | Bonding failure |
Conclusion: EVA mesh is only suitable for occasional washing within 5 cycles or fully disposable non-wash products. Choose PA or PES mesh for heavy wash resistance demands.
Thermal Aging & Temperature Resistance Test
Test Condition: Dry heat aging at 70℃ for 0, 100, 300, 500 hours
Bonded Assembly: EVA foam combined with non-woven fabric
| Aging Time (h) | Peel Strength (N/25mm) | Strength Retention | Appearance Change | Foam Status |
|---|---|---|---|---|
| 0 | 13.8 | 100% | No change | No shrinkage |
| 100 | 10.5 | 76% | Slight yellowing | No shrinkage |
| 300 | 6.2 | 45% | Obvious yellowing and brittleness | Minor foam shrinkage |
| 500 | 3.0 | 22% | Severe embrittlement | Foam shrinkage over 5% |
Conclusion: EVA mesh cannot serve under long-term high temperature above 70℃. PA and PES materials are applicable for working temperature exceeding 100℃.
Air Permeability Test of Different Mesh Weights
Test Standard: ISO 9237, airflow velocity tested under 100 Pa pressure difference
Baseline Data: Original air permeability of 30 g/m² PP non-woven: 1500 mm/s
| Sample Type | Airflow Velocity (mm/s) | Permeability Retention Rate | Hand Feeling Score (1-5) |
|---|---|---|---|
| Blank Fabric | 1500 | 100% | 5 |
| EW-60 (10 g/m²) | 1250 | 83% | 4.8 |
| EW-70 (20 g/m²) | 1080 | 72% | 4.5 |
| EW-70 (35 g/m²) | 850 | 57% | 4.0 |
| Equivalent 20 g/m² EVA Solid Film | ＜50 | ＜4% | 2.0 |
Conclusion: Lightweight EVA mesh retains over 80% original air permeability, ideal for masks, protective clothing and other breathable products.
Low Temperature Bending & Flexibility Test
Test Method: Freeze bonded composite sheets at -5℃, -10℃, -20℃ for 24 hours, bend 180° around 20mm round rod to check cracking status.
| Test Temperature | Bending Result | Post-bend Strength Retention | Phenomenon |
|---|---|---|---|
| 0℃ | No cracks | 95% | Flexible texture |
| -5℃ | Tiny surface cracks | 82% | Slightly brittle |
| -10℃ | Visible cracks and partial delamination | 55% | Brittle fracture tendency |
| -20℃ | Complete brittle breakage | ＜10% | Unusable |
Conclusion: Stable performance above 0℃. Brittleness risk occurs below -5℃, not applicable for freezing environment and winter outdoor sports goods.
Professional Industrial Application Cases
Proven hot-melt adhesive solutions delivering performance, compliance, and efficiency across global industries.
Heated Mouse Pad Made Using a Solvent-Free Multi-Layer Laminating Process
Demand
Maintain soft foldable property, comply with EN71 toy safety standard, lamination temperature below 70℃ to avoid foam shrinkage.
Solution
Adopt EW-60 20 g/m² ultra-low temperature soft mesh, low-pressure short-time hot pressing process.
Result & Impact
Stable bonding after 5000 repeated bends without delamination. Passed EN71 heavy metal test with zero VOC detected. Production cost cut by 50% compared with imported adhesive film, annual consumption reaches 400,000 square meters.
PP Non-woven Seam Sealing for Disposable Medical Protective Suit
Demand
Seam strength ≥10 N/25mm, moisture permeability close to original fabric, ISO 10993-10 skin safety compliance.
Solution
EW-60 12 g/m² lightweight mesh applied on overlapping seams, continuous roller lamination.
Result & Impact
Sealing strength hits 13 N/25mm meeting standard requirement. Moisture vapor transmission rate reaches 3200 g/m²/24h. Negative skin irritation test result, obtained CE certification, supplied 2 million pieces urgently.
Spiral Bonding for Eco-friendly Paper Straw
Demand
No delamination after 30-minute immersion in 80℃ hot water, support 150 m/min high-speed production.
Solution
EW-70 10 g/m² ultra-thin mesh matched spiral winding and hot shaping process.
Result & Impact
Stable bonding in hot water, peel strength meets paper bonding standard. Production efficiency greatly improved, manufacturing cost reduced by 20%, annual usage volume 1 million square meters.
XPE Foam Sound Insulation Composite for Automotive Interior
Demand
Low VOC and odor level, stable performance after 240-hour thermal aging at 70℃, peel strength ≥8 N/25mm.
Solution
EW-70 25 g/m² medium-weight mesh, surface activation treatment plus forced cooling after pressing.
Result & Impact
Final peel strength 10.5 N/25mm, 78% strength retention after aging. Odor and VOC indexes pass automotive inspection standards
Lamination Process
Preparation & Placement
Clean and dry bonding surfaces thoroughly. Sandwich mesh web between two materials.
Hot Pressing
Recommended Optimal Parameter: 75℃ / 0.15 MPa / 12 seconds.
Cooling & Inspection
Conduct subsequent processing after complete cooling. Verify overall bonding stability.
Note: Not applicable for high temperature working environments or frequent repeated washing.
Customization & Supply
Frequently Asked Questions
Why choose EVA mesh web over other materials?
Is it suitable for EVA foam bonding?
What is the difference between EW-60 and EW-70?
Are there any other models of the EVA Hot Melt Adhesive Mesh Web?
Get Technical Support
Contact us to obtain free samples, technical datasheets, and custom quotations.
Email Us
vomeltsales@163.com
Call Us
+86 17712662793
Factory Address
No. 36 Zhonglu Development Zone, Pingwang Town, Wujiang District, Suzhou City, Jiangsu Province